Wafer dicing blade consisting of multiple layers

ABSTRACT

The present invention provides a multi-layered diamond dicing blade. More particularly, the blade is a multi-layered dicing blade comprising an inner layer with a first set of diamond particles and an outer layer overlying the inner layer. The inner layer extends to the outermost periphery of the dicing blade. The outer layer comprises a second set of diamond particles having a size smaller than the first set of diamond particles.

FIELD OF THE INVENTION

[0001] This invention relates to precision cutting of discrete devicessuch as semiconductor devices, more particularly, to a diamond dicingblade used for efficient and symmetric cutting with reduced chipping.

DISCUSSION OF THE RELATED ART

[0002] There are many prior art discrete devices which are formed as aplurality of substrates integrally formed in a wafer or the like whichrequire intermediate cuts and/or separation into individual subunits asa last step in the fabrication process. Examples of such discretedevices are semiconductor devices. Most, but not all, of the devices areformed in silicon-based wafers. A preferred technique for separating thesub-units is to saw through the wafer in a procedure referred to as“dicing.” The device used to perform the cutting is referred to as adicing blade. For cutting operations requiring high precision (+/−0.5micron), diamond blades have been preferred, especially in theproduction of semiconductor devices, because they form precisely placedcuts.

[0003] However, these prior art diamond blades still suffer fromperformance variability manifested in the asymmetric chipping of thewafer due to the forces generated when pieces of silicon particlesloosen from the wafer between the rotating dicing blade and the siliconwafers being cut.

[0004] For instance, as shown in FIG. 1a, silicon wafer 8 having afrontside 10 and backside 12 is diced by a dicing blade 6 with largediamond particles 14, with a mean particle size of about 5-6 microns.Large diamond particles 14 allow for an increased feed rate orthroughput and produce good backside chipping 18. However, when largeparticles 14 are used they present the problem of poor frontsidechipping 16 due to the increased contact area/pressure between the largeparticle 14 and frontside 10. Hence, symmetric dicing on the frontside10 and backside 12 is problematic. The large degree of frontsidechipping is especially a problem because of its proximity to thefabricated circuitry which is located on wafer frontside 10.

[0005] In contrast, as shown in FIG. 1b, silicon wafer 8 having afrontside 10 and backside 12 may be diced by a dicing blade 4 with smalldiamond particles 20, with a mean particle size of about 1-2 microns.The small particle 20 provides minimal contact area with frontside 10thereby allowing minimal pressure and producing good frontside chipping3. But, small diamond particles 20 do not cut as efficiently as largeparticles 14 and using small particles 14 creates pressure buildup atthe leading edge of the dicing blade 4 thereby causing chips to breakout(“slivering”), creating poor backside chipping 2.

[0006] Therefore what is needed is a diamond dicing blade which producesefficient, symmetric cuts with reduced chipping on both the frontsideand backside of a wafer.

SUMMARY OF THE INVENTION

[0007] The present invention provides a multi-layered diamond dicingblade. More particularly, the blade is a multi-layered dicing bladecomprising an inner layer with a first set of diamond particles and anouter layer overlying the inner layer. The inner layer extends to theoutermost periphery of the dicing blade. The outer layer comprises asecond set of diamond particles having a size smaller than the first setof diamond particles. The first set of diamond particles makes initialcontact with the silicon wafer penetrating the bare silicon. The secondset of diamond particles of the dicing blade provides a fine finish.

[0008] The above advantages and features of the invention will be moreclearly understood from the following detailed description which isprovided in connection with the accompanying drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

[0009]FIG. 1(a) illustrates an exploded side sectional profile of aconventional dicing blade with large diamond particles;

[0010]FIG. 1(b) illustrates an exploded side sectional profile of aconventional dicing blade with small diamond particles;

[0011]FIG. 2 illustrates a spindle mounted dicing blade of the presentinvention performing a cutting action across a wafer;

[0012]FIG. 3 illustrates an exploded side sectional profile of a dicingblade of FIG. 2 of the present invention;

[0013]FIG. 4 illustrates an exemplary embodiment of a plating tank forfabricating the dicing blade of the present invention; and

[0014]FIG. 5 illustrates an exploded side sectional view of an annularhub mounted upon a rotatable spindle for fabricating the dicing blade ofthe present invention.

DETAILED DESCRIPTION OF THE INVENTION

[0015] The present invention will be described in connection with anexemplary embodiment of a dicing blade illustrated in FIG. 2-3. Otherembodiments may be utilized and structural or logical changes may bemade without departing from the spirit or scope of the presentinvention. Although the invention is illustrated in the drawings inconnection with severing semiconductor devices from wafers, theinvention may also be used to cut through other objects as well. Likeitems are referred to by like reference numerals throughout thedrawings.

[0016] Referring now to FIG. 2, there is shown a wafer saw 28 formed bya hub 30 and a dicing blade 26 of the present invention. The dicingblade 26 further comprises an outer layer B containing small diamondparticles 24 overlying and inner layer A containing large diamondparticles 22. The hub 30 is mounted upon a rotatable spindle 32. Theblade 26 is positioned in relation to a wafer 8 in order to make aplurality of parallel cuts 34 during successive passes of the rotatingblade 26. After the wafer has been cut into a plurality of strips, thewafer is rotated 90° and a plurality of second cuts are made. The secondcuts segment a plurality of dies from the wafer 8.

[0017] As shown in FIG. 4, construction of the dicing blade 26 beginswith a formed aluminum hub 30 mounted upon a rotatable spindle 32supported by a support 31. An 0-ring seal or the like 36 is placedadjacent the hub 30 radially interiorly from the perimeter to serve as amask and permits selective plating only on the annular area 38 where thedicing blade 26 is to be formed. The plating tank 40 (FIG. 5) includes anickel plating solution 42 having large diamond particles 22 suspendedtherein. The nickel plating solution may be a nickel sulfamate solutionsold under various trademarks, such as Allied Kelite, Enthone, SelRex,etc. The large diamond particles have a mean particle size of about 4microns to about 8 microns. It is maintained in suspension by eithermechanical or air agitation. The nickel plating tank may be of variousconfigurations (round, square, etc.). The nickel plating solution isheated to operating temperature by using immersion heaters and automatictemperature controls to maintain a preset temperature to +/−2%. Purenickel anodes 44 are located within the tank and at an equal spacingabout the hub supporting spindle 32 (cathode). The power or current froma DC power supply is regulated to a current density (amperes per squarefoot of plating area) suggested by the supplier of the plating solution.

[0018] The spindle 32 is rotated (arrow A) at a predetermined speed fora predetermined duration. Rotation is thereafter stopped to permit thelarge diamond particles 22 to settle on the exposed annular hub 30.Rotation is subsequently reversed and then stopped. This cycle isrepeated until a desired thickness of nickel and large diamond particle22 composition is reached. Generally, the deposition rate of nickelsulfamate is approximately 0.001 inches (25.4 mm) per hour. This processis repeated utilizing small diamond particles 24, which have a meanparticle size in the range of about 2 microns to about 4 microns, tofabricate a dicing blade 26 (FIG. 3) with an outer layer B overlyinginner layer A containing large diamond particles 22. Next, the outermostperiphery of the dicing blade is shaped to provide a sharp, precisecontact point with, for instance, a semiconductor wafer.

[0019] Referring now to FIG. 3, there is shown an exploded sidesectional view of the dicing blade 26 of the present invention. FIG. 3shows a silicon wafer 8 having a frontside 10 and backside 12 beingdiced by a dicing blade 26 with an outer layer containing small diamondparticles 24 overlying an inner layer containing large diamond particles22. As noted, the small diamond particles 24 have a mean particle sizeof about 2 microns to about 4 microns and the large diamond particles 22have a mean particle size of about 4 microns to about 8 microns. Blade26 has an inner layer A with a maximum thickness of about 1.0 to about1.2 millimeters and an outer layer B with a maximum thickness of about0.3 to about 0.5 millimeters. As illustrated, inner layer A extends tothe outermost periphery of the dicing blade 26. Hence, large diamondparticles 22 of the dicing blade make initial contact with the siliconwafer 8 penetrating the bare silicon, allowing for increased throughputand efficiency. Next, small diamond particles 24 of the dicing bladeprovides a symmetric, fine finish. In this way, the combination of largeparticles 22 and small particles 24 provide good frontside clipping 30and good backside chipping 28 of a wafer.

[0020] Hence, the invention provides a multi-layered dicing bladecomprising an inner layer with a first set of diamond particles and anouter layer overlying the inner layer. The inner layer extends to theoutermost periphery of the dicing blade. The outer layer comprises asecond set of diamond particles having a size smaller than the first setof diamond particles.

[0021] Although the invention has been described above in connectionwith exemplary embodiments, it is apparent that many modifications andsubstitutions can be made without departing from the spirit or scope ofthe invention. In particular, although the invention is described withreference to a two layer dicing blade, it should be appreciated thatmultiple layers of large and small diamond particles may be utilized.Accordingly, the invention is not to be considered as limited by theforegoing description, but is only limited by the scope of the appendedclaims.

What is claimed as new and desired to be protected by Letters Patent ofthe United States is:
 1. A dicing blade comprising: an inner layercontaining a first set of dicing particles and an outer layer containinga second set of dicing particles overlying said inner layer, said secondset of dicing particles having a mean particle size which is smallerthan a mean particle size of said first set of dicing particles; andwherein said inner layer extends beyond said outer layer to theoutermost periphery of said dicing blade.
 2. The blade of claim 1wherein said dicing particles are diamond particles.
 3. The blade ofclaim 1 wherein said first set of dicing particles have a mean particlesize of about 4 microns to about 8 microns.
 4. The blade of claim 1wherein said second set of dicing particles have a mean particle size ofabout 2 microns to about 4 microns.
 5. The blade of claim 1 wherein saidinner layer has a maximum thickness of about 1.0 to about 1.2millimeters.
 6. The blade of claim 1 wherein said outer layer has amaximum thickness of about 0.3 to about 0.5 millimeters.
 7. The blade ofclaim 1 wherein the dicing blade is formed of at least two layers. 8.The blade of claim 7 wherein said dicing particles are diamondparticles.
 9. The blade of claim 7 wherein said first set of dicingparticles have a mean particle size of about 4 microns to about 8microns.
 10. The blade of claim 7 wherein said second set of dicingparticles have a mean particle size of about 2 microns to about 4microns.
 11. The blade of claim 7 wherein said inner layer has a maximumthickness of about 1.0 to about 1.2 millimeters.
 12. The blade of claim7 wherein said outer layer has a maximum thickness of about 0.3 to about0.5 millimeters.
 13. A dicing blade comprising the combination of: atleast two layers wherein at least one of the two layers comprises aninner layer containing a first set of dicing particles having a meanparticle size range of about 4 to 8 microns; least one of the two layerscomprises an outer layer overlying said inner layer, said outer layercontaining a second set of dicing particles having a mean particle sizerange of about 2 to 4 microns; wherein said second set of dicingparticles has a smaller mean particle size than said first set of dicingparticles; and wherein said inner layer extends beyond said outer layerto the outermost periphery of said dicing blade.
 14. The blade of claim13 wherein said dicing particles are diamond particles.
 15. The blade ofclaim 13 wherein said inner layer has a maximum thickness of about 1.0to about 1.2 millimeters.
 16. The blade of claim 13 wherein said outerlayer has a maximum thickness of about 0.3 to about 0.5 millimeters. 17.A dicing saw comprising: a rotatable spindle; and at least one dicingblade coupled to said spindle, said dicing blade comprising: an innerlayer containing a first set of dicing particles and an outer layercontaining a second set of dicing particles overlying said inner layer,said second set of dicing particles having a mean particle size which issmaller than a mean particle size of said first set of dicing particles;and wherein said inner layer extends beyond said outer layer to theoutermost periphery of said dicing blade.
 18. The saw of claim 17wherein said dicing particles are diamond particles.
 19. The saw ofclaim 17 wherein said first set of dicing particles have a mean particlesize of about 4 microns to about 8 microns.
 20. The saw of claim 17wherein said second set of dicing particles have a mean particle size ofabout 2 microns to about 4 microns.
 21. The saw of claim 17 wherein saidinner layer has a maximum thickness of about 1.0 to about 1.2millimeters.
 22. The saw of claim 17 wherein said outer layer has amaximum thickness of about 0.3 to about 0.5 millimeters.
 23. The saw ofclaim 17 wherein said saw is used for dicing semiconductor wafers. 24.An apparatus for dicing objects comprising: a first support forsupporting said objects; a second support for supporting a dicing saw todice said objects, said dicing saw comprising: a rotatable spindle; andat least one dicing blade coupled to said spindle, said dicing bladecomprising: an inner layer containing a first set of dicing particlesand an outer layer containing a second set of dicing particles overlyingsaid inner layer, said second set of dicing particles having a meanparticle size which is smaller than a mean particle size of said firstset of dicing particles; and wherein said inner layer extends beyondsaid outer layer to the outermost periphery of said dicing blade. 25.The apparatus of claim 24 wherein said dicing particles are diamondparticles.
 26. The apparatus of claim 24 wherein said first set ofdicing particles have a mean particle size of about 4 microns to about 8microns.
 27. The apparatus of claim 24 wherein said second set of dicingparticles have a mean particle size of about 2 microns to about 4microns.
 28. The apparatus of claim 24 wherein said inner layer has amaximum thickness of about 1.0 to about 1.2 millimeters.
 29. Theapparatus of claim 24 wherein said outer layer has a maximum thicknessof about 0.3 to about 0.5 millimeters.
 30. The apparatus of claim 24wherein said objects are semiconductor wafers.
 31. An apparatus fordicing semiconductor wafers comprising: a first wafer support; a secondsupport for supporting a dicing saw to dice a wafer placed on saidsupport, said dicing saw comprising: a rotatable spindle; and at leastone dicing blade coupled to said spindle, said dicing blade comprising:an inner layer containing a first set of dicing particles and an outerlayer containing a second set of dicing particles overlying said innerlayer, said second set of dicing particles having a mean particle sizewhich is smaller than a mean particle size of said first set of dicingparticles; and wherein said inner layer extends beyond said outer layerto the outermost periphery of said dicing blade.
 32. The apparatus ofclaim 31 wherein said dicing particles are diamond particles.
 33. Theapparatus of claim 31 wherein said first set of dicing particles have amean particle size of about 4 microns to about 8 microns.
 34. Theapparatus of claim 31 wherein said second set of dicing particles have amean particle size of about 2 microns to about 4 microns.
 35. Theapparatus of claim 31 wherein said inner layer has a maximum thicknessof about 1.0 to about 1.2 millimeters.
 36. The apparatus of claim 31wherein said outer layer has a maximum thickness of about 0.3 to about0.5 millimeters.
 37. A method of fabricating a dicing blade comprisingthe acts of: forming an inner blade layer containing a first set ofdicing particles and an outer layer overlying said inner layer, saidouter layer containing a second set of dicing particles having a meanparticle size which is smaller than a mean particle size of first set ofdicing particles; and wherein said inner layer is formed to extendbeyond said outer layer to the outermost periphery of said dicing blade.38. The method of claim 36 wherein said dicing particles are diamondparticles.
 39. The method of claim 36 wherein said dicing bladecomprises as least two layers.
 40. The method of claim 29 wherein saiddicing blades are used to dice semiconductor wafers.
 41. A method offabricating a dicing saw comprising the acts of: providing a spindle;forming at least one dicing blade coupled to said spindle, said dicingblade being formed by the acts of: forming an inner layer containing afirst set of dicing particles and an outer layer containing a second setof dicing particles overlying said inner layer, said second set ofdicing particles having a mean particle size which is smaller than amean particle size of said first set of dicing particles; and whereinsaid inner layer extends to the outermost periphery of said dicingblade.
 42. The method of claim 41 wherein said dicing particles arediamond particles.
 43. A method of fabricating a dicing blade comprisingthe acts of: providing a cathode on which plating can occur; providing afirst plating bath including a first set of large dicing particles andanodes about equally spaced from said cathode when emersed in said firstplating bath; emersing said cathode in said first plating bath; rotatingsaid cathode within said first plating bath at a predetermined speed fora predetermined duration to form an inner layer on said cathodecontaining said large dicing particles; providing a second plating bathincluding a second set of small dicing particles and anodes aboutequally spaced from said cathode when emersed in said second platingbath; emersing said cathode in said second plating bath; rotating saidcathode within said second plating bath at a predetermined speed for apredetermined duration to form an outer layer on said cathode containingsaid small dicing particles; and forming said inner and outer layer suchthat said inner layer extends beyond said outer layer to the outermostperiphery of said dicing blade.
 44. The method of claim 43 furthercomprising the act of stopping and reversing said rotation until adesired thickness of said inner layer is reached.
 45. The method ofclaim 43 wherein said first set of dicing particles have a mean particlesize of about 4 microns to about 8 microns.
 46. The method of claim 43wherein said second set of dicing particles have a mean particle size ofabout 2 microns to about 4 microns.
 47. The method of claim 43 whereinsaid inner layer has a maximum thickness of about 1.0 to about 1.2millimeters.
 48. The method of claim 43 wherein said outer layer has amaximum thickness of about 0.3 to about 0.5 millimeters.
 49. The methodof claim 43 wherein said particles are diamond particles.